Tipo do documento: Tese
Título: Comparação das alterações dimensionais lineares em modelos de gesso pedra tipo IV obtidos de moldes de siliconas de condensação e de adição em períodos diferentes de vazamento
Título(s) alternativo(s): Dimensional alteration of dental stone type 4 casts acquired by condensation and addition silicone poured at differents periods
Autor: Fares, Nasser Hussein 
Primeiro orientador: Nary Filho, Hugo
Primeiro coorientador: Nagem Filho, Halim
Resumo: Foi avaliada a estabilidade dimensional de duas marcas comerciais de siliconas, sendo uma de condensação e outra de adição em função de diferentes tempos de vazamento. Um modelo padrão metálico foi elaborado com dois pilares com mesma altura, diâmetro e distância entre si. A partir desse modelo padrão foram obtidos 80 moldes através da técnica de dupla moldagem com um alívio uniforme de 1 mm em moldeiras parciais de alumínio perfurada rígida, de estoque . Um total de 80 amostras foram confeccionadas, sendo 40 com silicona de condensação e outras 40 com silicona de adição. Os tempos para vazamento com o gesso tipo IV foram de 30 minutos, 24 horas, 72 horas e uma semana para todas as condições experimentais testadas respectivamente após a moldagem. As medições foram feitas em três áreas distintas de cada pilar: diâmetro oclusal, altura e a distância entre os mesmos também foi registrada. Um aparelho escâner tridimensional para digitalização da imagem e um software empregado para as mensurações. Os resultados nos tempos para vazamento de 30 minutos e 24 horas foram os melhores para se obter o modelo de gesso para ambos os materiais. A silicona de condensação pode ser utilizada com segurança desde que o vazamento seja no máximo até 24horas.
Abstract: Dimensional stability of two silicones impression materials, condensation and addition, was assessed regarding poured periods. A metal master model was constructed with two implant abutments with same height, diameter and same distance between the abutmens. Eighty models of the master model were obtained with the two times impression technique. All partial aluminum stock tray were relieved in 1 mm. The sample was divided in two groups: 1) 40 models acquired by condensation silicone and 2) 40 models acquired by addition silicone. The dental stone type 4 were poured before molding at periods: 30 minutes, 24 hours, 72 hours andn one week. The OrthoAnalyzer-2010 was used to measure three zones of each abutment: oclusal diameter, height and distance between the abutments. The data was analyzed and results were better at periods 30 minutes and 24 hours with both materials. The condensation silicone can be well utilized provided the poured period should be at least 24 hours.
Palavras-chave: MATERIAL PARA MOLDAGEM ODONTOLÓGICA
SILICONA
IMPLANTES DENTÁRIOS
DENTAL IMPRESSION MATERIAL
SILICONE
DENTAL IMPLANTS
Área(s) do CNPq: CIENCIAS DA SAUDE::ODONTOLOGIA
Idioma: por
País: BR
Instituição: IASCJ - Universidade Sagrado Coração
Sigla da instituição: USC
Departamento: Ciências da Saúde e Biológicas
Programa: Implantologia
Citação: FARES, Nasser Hussein. Dimensional alteration of dental stone type 4 casts acquired by condensation and addition silicone poured at differents periods. 2012. 47 f. Tese (Doutorado em Biologia Oral - Implantologia) - IASCJ - Universidade Sagrado Coração, Bauru, 2012.
Tipo de acesso: Acesso Aberto
URI: http://localhost:8080/tede/handle/tede/135
Data de defesa: 28-Fev-2012
Aparece nas coleções:Doutorado em Implantologia

Arquivos associados a este item:
Arquivo TamanhoFormato 
tese_nasser_hussein_fares.pdf2,57 MBAdobe PDFBaixar/Abrir Pré-Visualizar


Os itens no repositório estão protegidos por copyright, com todos os direitos reservados, salvo quando é indicado o contrário.