Export iten: EndNote BibTex

Please use this identifier to cite or link to this item: https://tede2.unisagrado.edu.br:8443/handle/tede/145
Full metadata record
DC FieldValueLanguage
dc.creatorSilva Neto, Genilson da-
dc.creator.Latteshttp://lattes.cnpq.br/6771013407934260por
dc.contributor.advisor1Francischone, Carlos Eduardo-
dc.contributor.advisor1Latteshttp://lattes.cnpq.br/5622847033913614por
dc.date.accessioned2015-09-14T13:12:53Z-
dc.date.available2012-10-02-
dc.date.issued2011-08-08-
dc.identifier.citationSILVA NETO, Genilson da. Comparative analysis of bond strength between systems ceramocerâmicos and metalocerâmico. 2011. 91 f. Tese (Doutorado em Biologia Oral - Implantologia) - IASCJ - Universidade Sagrado Coração, Bauru, 2011.por
dc.identifier.urihttp://localhost:8080/tede/handle/tede/145-
dc.description.resumoO objetivo deste estudo foi realizar uma caracterização quantitativa e qualitativa das interfaces em sistemas metalocerâmicos e cerâmicos atualmente disponíveis no mercado para fins odontológicos. Para isto, padrões cilíndricos (6,5 mm comprimento x 6 mm diâmetro) contendo o material da infra-estrutura/recobrimento foram confeccionados e divididos em 10 grupos: Wiron 99/Kiss (WK), In-Ceram Zirconia/Vita VM7 (ICZ-VM7), Ceramill White Core Zirconia/Nobel Rondo e Nobel Rondo Press (CWCZ-NR e CWCZ-NRP); Ceramill Colored Core Zirconia/Nobel Rondo e Nobel Rondo Press (CCCZ-NR e CCCZ-NRP), Procera White Core Zirconia/Nobel Rondo e Nobel Rondo Press (PWCZ-NR e PWCZ-NRP); Procera Colored Core Zirconia/Nobel Rondo e Nobel Rondo Press (PCCZ-NR e NRP). Todos os grupos foram submetidos ao teste de cisalhamento até ruptura (análise quantitativa) e MEV/EDS (análise qualitativa). Os valores médios obtidos (em MPa) após o cisalhamento foram: WK (36,12±3,86); ICZ-VM7 (34,20±5,85); CWCZ-NR e NRP (33,69±8,75 e 51,44±7,39); CCCZ-NR e NRP (36,00±9,05 e 36,52±3,77); PWCZ-NR e NRP (48,23±7,32 e 46,50±10,87); PCCZ-NR e NRP (37,16±8,37 e 28,35±9,21). As análises por MEV (ES,ERD) e EDRX comprovaram a presença de fraturas coesivas tanto no grupo WK quanto nos outros grupos ceramocerâmicos, exceto para o grupo PWCZ-NR que apresentou fratura mista na cerâmica de recobrimento. Todos os grupos cerâmicos testados mostraram resistência ao cisalhamento próxima ao grupo controle. Entretanto, os grupos PWCZ-NR e NRP mostraram valores superiores.por
dc.description.abstractThe aim of this study was to perform quantitative and qualitative characterization of metalloceramic and ceramic interfaces commercially available in the market for dental purposes. For this, cylindrical patterns (6.5 mm in height x 6 mm in diameter) were fabricated and divided into 10 groups: Wiron 99/Kiss (WK), In-Ceram Zirconia/Vita VM7 (ICZ-VM7), Ceramill White Core Zirconia/Nobel Rondo and Nobel Rondo Press (CWCZ-NR and CWCZNRP); Ceramill Colored Core Zirconia/Nobel Rondo and Nobel Rondo Press (CCCZ-NR and CCCZ-NRP), Procera White Core Zirconia/ Nobel Rondo and Nobel Rondo Press (PWCZ-NR and PWCZ-NRP); Procera Colored Core Zirconia/Nobel Rondo and Nobel Rondo Press (PCCZ-NR and NRP). All groups were submitted to a shear bond strength test until fracture (quantitative) and SEM/EDS (qualitative analysis). Mean shear values (MPa) were: WK (36.12±3.86); ICZ-VM7 (34.20±5.85); CWCZ-NR and NRP (33.69±8.75 and 51.44±7.39); CCCZ-NR and NRP (36.00±9.05 and 36.52±3.77); PWCZ-NR and NRP (48.23±7.32 and 46.50±10.87); PCCZ-NR and NRP (37.16±8.37 and 28.35±9.21). MEV(EDS,EDR) and EDRX characterization determined cohesive fractures in both WK and ceramic groups, except on the PWCZ-NR group, wich showed mixed fractures with small crest and islets of veneering material. All ceramic interfaces provided shear bond strength values near to that control group. However, groups PWCZ-NR and NRP showed superior values.eng
dc.description.provenanceMade available in DSpace on 2015-09-14T13:12:53Z (GMT). No. of bitstreams: 1 tese_genilson_da_silva_neto.pdf: 15278821 bytes, checksum: 1ae112ab67ebb54c1099ed074d828111 (MD5) Previous issue date: 2011-08-08eng
dc.formatapplication/pdfpor
dc.languageporpor
dc.publisherIASCJ - Universidade Sagrado Coraçãopor
dc.publisher.departmentCiências da Saúde e Biológicaspor
dc.publisher.countryBRpor
dc.publisher.initialsUSCpor
dc.publisher.programImplantologiapor
dc.rightsAcesso Abertopor
dc.subjectRESISTÊNCIA AO CISALHAMENTOpor
dc.subjectPORCELANAS ODONTOLÓGICASpor
dc.subjectÓXIDO DE ZIRCÔNIOpor
dc.subjectLIGAS DE NI-CRpor
dc.subjectSHEAR BOND STRENGTHeng
dc.subjectDENTAL CERAMICSeng
dc.subjectZIRCONIA OXIDEeng
dc.subjectNI-CR ALLOYSeng
dc.subject.cnpqCIENCIAS DA SAUDE::ODONTOLOGIApor
dc.titleAnálise comparativa da resistência de união entre sistemas ceramocerâmicos e metalocerâmicopor
dc.title.alternativeComparative analysis of bond strength between systems ceramocerâmicos and metalocerâmicoeng
dc.typeTesepor
Appears in Collections:Doutorado em Implantologia



Items in TEDE are protected by copyright, with all rights reserved, unless otherwise indicated.