Título: Avaliação biomecânica da resistência ao torque de inserção de diferentes sistemas de implantes
Título(s) alternativo(s): Biomechanical evaluation of the resistance to insertion torque of different implant systems
Autor: Sedmak, José Felício 
Primeiro orientador: Nary Filho, Hugo
Resumo: Objetivo: conhecer, in vitro, a resistência ao torque de inserção, de diferentes sistemas de implantes, com a finalidade de se identificar possíveis riscos ao uso clínico. Materiais e métodos: foram utilizados três grupos (cinco unidades cada), da seguinte forma: A) Implante Osseotite, 4 x 13 mm, hexagonal externo (Biomet 3i); B) Implante Bonelike 4 x 13 mm, hexagonal externo (Biotechnology); C) Implante Mk III RP, 3,75 x 13 mm, hexagonal externo (Nobel Biocare). Foram usadas chaves de inserção descartáveis, sendo que cada conjunto foi submetido ao teste de torção (ASTM F543:2007) para a determinação do torque de ruptura, ângulo de ruptura, torque de escoamento em dois graus e torque máximo. Resultados: foram obtidos os valores médios dos parâmetros analisados para os respectivos grupos: torque de ruptura (N/cm2): 218,00; 132,00; 132,00; deformação angular de ruptura (°): 29,04; 39,94; 31,92; torque de escoamento em 2° (N/cm2): 177,00; 153,00; 140,00; torque máximo (N/cm2): 222,00; 172,00; 142,00. Conclusões: os limites de resistência ao torque dos sistemas analisados foram superiores às necessidades clínicas, oferecendo segurança às suas aplicações, desde que respeitados os seus limites mecânicos, sendo que, o Grupo A (Biomet 3i) apresentou os melhores resultados entre os grupos.
Abstract: Objective: to, in vitro resistance to insertion torque of different implant systems, for the purpose of identifying possible risks to clinical use. Methods: A total of three groups (five units each), as follows: A) Implant Osseotite, 4 x 13 mm, external hexagonal (Biomet 3i); B) Deploy Bonelike 4 x 13 mm, external hexagonal (Biotechnology); C) Implant Mk III RP, 3.75 x 13 mm, external hexagonal (Nobel Biocare). Disposable insert keys were used, and each set was subjected to the torque test (ASTM F543: 2007) for determining the rupture torque, break angle flow in two degrees torque and maximum torque. Results: we obtained the average values of the parameters analyzed for the respective groups: Break torque (N / cm2): 218.00; 132.00; 132.00; angular deformation of rupture (°): 29.04; 39.94; 31.92; torque flow at 2 ° (N / cm2): 177.00; 153.00; 140.00; Maximum torque (N / cm2): 222.00; 172.00; 142.00. Conclusions: the resistance limits the torque of the analyzed systems were superior to clinical needs, offering security to their applications, since their mechanical limits respected, and, Group A (Biomet 3i) showed the best results among the groups.
Palavras-chave: Estresse mecânico
Implantes dentários
Torque
Mechanical stress
Dental implants
Torque
Área(s) do CNPq: CIENCIAS DA SAUDE::ODONTOLOGIA
Idioma: por
País: Brasil
Instituição: Universidade do Sagrado Coração
Sigla da instituição: USC
Departamento: Ciências da Saúde e Biológicas
Programa: Implantologia
Citação: SEDMAK, José Felício. Avaliação biomecânica da resistência ao torque de inserção de diferentes sistemas de implantes. 2015. 41 f. Dissertação (Mestrado em Biologia Oral - Implantologia) - Universidade do Sagrado Coração, Bauru, 2015.
Tipo de acesso: Acesso Aberto
URI: http://tede2.usc.br:8080/jspui/handle/tede/295
Data de defesa: 8-Sep-2015
Appears in Collections:Mestrado em Implantologia

Files in This Item:
File Description SizeFormat 
dissertacao_jose_sedmak.pdfDocumento completo552,3 kBAdobe PDFView/Open ???org.dspace.app.webui.jsptag.ItemTag.preview???


Items in TEDE are protected by copyright, with all rights reserved, unless otherwise indicated.