Título: Obtenção de placas a base de pvc reciclado para uso em construção civil
Título(s) alternativo(s): Obtaining of plates based on recycled pvc for use in civil construction
Autor: Gentil Junior, Geraldo Ari 
Primeiro orientador: Chaves, Márcia Rodrigues de Morais
Primeiro coorientador: Tavares, Beatriz Antoniassi
Resumo: O desenvolvimento sustentável dos processos industriais está associado ao uso pós-consumo de seus produtos. Dentre os problemas ambientais, se destaca a grande produção de resíduos de pós-consumo de materiais poliméricos, em especial o Policloreto de Vinila (PVC), utilizado para confecção de produtos de vestuário, desportivo, construção civil, etc. Por outro lado, o uso de derivados de madeira pode levar ao desmatamento. Grande parte do desmatamento contínuo é impulsionada pela demanda de madeira utilizada na construção civil, além de parte desta madeira, transforma-se em resíduo. O desenvolvimento de materiais compósitos, tais como a madeira plástica, é fundamental para garantir a oferta de produtos ao setor de construção civil, ao mesmo tempo em que aproveita os resíduos industriais e urbanos. A madeira plástica pode apresentar características físicas, químicas e mecânicas satisfatórias ou superiores para substituir plenamente o uso da madeira ou do plástico. A escolha da utilização do bambu na produção das placas foi devido à expectativa em agregar alta resistência à ruptura e impacto ao produto proposto, e motivado pela escassez de estudos sobre materiais compósitos com tal formação. O objetivo deste trabalho foi preparar, caracterizar e avaliar economicamente placas de madeira plástica composta de resíduos de PVCr + madeira e PVCr + bambu, a fim de utilizá-las como componentes da construção civil. As placas (17 cm x 17 cm x 1,0 cm) de PVC + serragem de madeira e PVC + bambu foram obtidas por injeção termomecânica das misturas dos materiais contendo 10, 20, 30 e 40% em peso de fibra vegetal. Dioctilftalato (DOP) 1% foi utilizado como plastificante e ligante. A pressão de injeção foi de 40% (64 toneladas) e as temperaturas nas zonas de aquecimento de injeção foram 165oC, 160oC, 150oC. Amostras das placas foram obtidas para determinação de dureza (Shore A), resistência a ruptura a tração e por flexão em três pontos (ASTM D790 e ASTM D638). Os resultados preliminares indicaram que a adição de fibras vegetais ao PVC reciclado diminui a resistência à ruptura por tração (até 60%), porém aumenta a resistência à ruptura por flexão (até 550%) e a dureza (até 18%), indicando um excelente potencial das placas de PVC reciclado para serem utilizadas na construção civil.
Abstract: The sustainable development of industrial processes is associated with the post-consumer use of its products. Among the environmental problems is the large production of post-consumer waste from polymeric materials, in particular, Polyvinyl chloride (PVC), used to make garments, sports, construction, etc. On the other hand, the use of wood derivatives can lead to deforestation. Much of the continuous deforestation is driven by the demand for wood used in construction. In addition, part of this wood becomes waste. The development of composite materials, such as plastic wood, is fundamental to guarantee the supply of products to the civil construction sector while taking advantage of industrial and urban waste. Plastic wood may have satisfactory or superior physical, chemical and mechanical characteristics to fully replace the use of wood or plastic. The choice of the use of bamboo in the production of the plates was due to the expectation of adding high resistance to rupture and impact to the product proposed, and motivated by the lack of studies on composite materials with such formation. The objective of this work was to prepare, characterize and economically evaluate plastic wood boards composed of PVCr + wood and PVCr + bamboo waste, in order to use them as components of the civil construction. The boards (17 cm x 17 cm x 1.0 cm) of PVC + wood sawdust and PVC + bamboo were obtained by thermomechanical injection of the blends of materials containing 10, 20, 30 and 40% by weight of vegetable fiber. Dioctyl phthalate (DOP) 1% was used as plasticizer and binder. The injection pressure was 40% (64 tons) and the temperatures in the injection heating zones were 165°C, 160°C, 150°C. Plates samples were obtained for determination of hardness (Shore A), tensile strength and three-point flexural strength (ASTM D790 and ASTM D638). Preliminary results indicated that the addition of vegetal fibers to the recycled PVC reduces tensile strength (up to 60%), but increases flexural strength (up to 550%) and hardness (up to 18%), indicating an excellent potential of recycled PVC boards for use in construction.
Palavras-chave: Madeira plástica
PVC
Bambu
Reciclagem
Aproveitamento de resíduos 
Wood-plastic
PVC
Bamboo
Recycling
Waste management
Área(s) do CNPq: CIENCIAS EXATAS E DA TERRA
Idioma: por
País: Brasil
Instituição: Universidade do Sagrado Coração
Sigla da instituição: USC
Departamento: Ciências da Saúde e Biológicas
Programa: Ciência e Tecnologia Ambiental
Citação: Gentil Junior, Geraldo Ari. Obtenção de placas a base de pvc reciclado para uso em construção civil. 2019. Dissertação (Ciência e Tecnologia Ambiental) - Universidade do Sagrado Coração, Bauru, 2019.
Tipo de acesso: Acesso Aberto
URI: https://tede2.usc.br:8443/handle/tede/472
Data de defesa: 17-Jun-2019
Appears in Collections:Mestrado em Ciência e Tecnologia Ambiental



Items in TEDE are protected by copyright, with all rights reserved, unless otherwise indicated.